Use Instructions - Dentsply Sirona UNIVERSAL STAIN Mode D'emploi

Use Instructions:

Framework Preparation:
Follow the current corresponding Directions for Use for preparing the
substructure material.
Directions for Use:
> Celtra Press zirconia reinforced lithium silicate - 50539994
> Celtra DUO zirconia reinforced lithium silicate - 50539985
> Cercon ht, Cercon xt - 50537617
> Ceramco PFZ porcelain for zirconia - 090862
> Cercon Ceram Kiss porcelain - 28078
> Ceramco3 porcelain - 301700
> Ceramco iC porcelain – 745-215
> Duceram Kiss porcelain – 22147
Stain & glaze application:
Note: If the stain or glaze inside the jar has separated, mix thoroughly with
a glass, plastic or zirconia spatula. Withdraw desired amount of Universal
Stain or Glaze from the jar and place it on the mixing palette. If a thinner
consistency is desired, dilute the material with the Dentsply Sirona Stain
and Glaze Liquid (REF 601315/15mL, 601350/50mL). (See Figure 1)
Apply a thin layer of the stain or glaze material all over the crown surface
in the usual manner using a brush. Make sure not to apply the glaze
material too thick or too thin. Too thin of a layer will result in a more
matte finish. Too thick of a layer can result in puddling and/or pitting of
the material. (See Figure 2)
If a more intensive shade effect is desired, it is achieved by several
staining applications and firings. However, the application of too many
stain layers can result in an unnatural shade effect.
Figure 1 Figure 2
3
Stain & glaze firing:
Please use the suggested furnace cycle/program shown below:
Pre-
Drying heat Low
(min) (min) Temp Heat Rate
Celtra Press
2 2 400°C 55°C/min
(full contour)
Celtra Press
(cutback or
2 2 400°C 55°C/min
2nd firing of
full contour)
Celtra DUO
2 2 500°C 55°C/min
Cercon ht
3 3 450°C 55°C/min
Ceramco
5 5 450°C 60°C/min
PFZ*
Cercon
2 3 450°C 55°C/min
Ceram Kiss
Ceramco3
3 3 650°C 70°C/min
Ceramco iC
3 3 500°C 35°C/min
Duceram
3 1 575°C 55°C/min
Kiss
* Drying time depends on the type of furnace
* Additional Stain/glaze and characterization firing cycles can be conducted with the same firing parameters.
Do not go below or above the temperature range 740°C to 950°C.
* Ceramco PFZ is not authorized for sale in Canada.
Hold
Vac Vac Hold Time
High Start Stop Time Air
Temp Temp Temp Vac (min)
760°C 0 0 0 2:00
750°C 0 0 0 2:00
820°C 0 0 0 1:30
820°C 0 0 0 1:30
850°C 0 0 0 0:30
800°C 0 0 0 1:00
935°C 0 0 0 0:30
750°C 500°C 750°C 1 1:30
890°C 0 0 0 1:00
4
Cool
Time
(min)
5
5
3
6
6
6
0
0
0